建築物における外装材料の経年劣化の評価に関する研究
https://kougei.repo.nii.ac.jp/records/2000004
https://kougei.repo.nii.ac.jp/records/20000041051f957-d0ce-48a4-ad21-01f2586b4cd9
| 名前 / ファイル | ライセンス | アクション |
|---|---|---|
Dcourse_61_abstract.pdf (368 KB)
|
|
| Item type | 学位論文 / Thesis or Dissertation(1) | |||||
|---|---|---|---|---|---|---|
| 公開日 | 2023-10-31 | |||||
| タイトル | ||||||
| タイトル | 建築物における外装材料の経年劣化の評価に関する研究 | |||||
| 言語 | ja | |||||
| 言語 | ||||||
| 言語 | jpn | |||||
| キーワード | ||||||
| 言語 | ja | |||||
| 主題Scheme | Other | |||||
| 主題 | 外装材料 | |||||
| キーワード | ||||||
| 言語 | ja | |||||
| 主題Scheme | Other | |||||
| 主題 | 長寿命化 | |||||
| キーワード | ||||||
| 言語 | ja | |||||
| 主題Scheme | Other | |||||
| 主題 | 経年劣化 | |||||
| 資源タイプ | ||||||
| 資源タイプ識別子 | http://purl.org/coar/resource_type/c_db06 | |||||
| 資源タイプ | doctoral thesis | |||||
| アクセス権 | ||||||
| アクセス権 | open access | |||||
| アクセス権URI | http://purl.org/coar/access_right/c_abf2 | |||||
| 著者 |
髙橋, 愛枝
× 髙橋, 愛枝 |
|||||
| 抄録 | ||||||
| 内容記述タイプ | Abstract | |||||
| 内容記述 | 有機系接着剤による外壁タイル張り工法の耐久性を明らかにするため，促進劣化試験（温冷繰返し試験）および屋外暴露試験を実施し，耐久性能の検証を行った。今回の実験範囲の結果，以下の知見を得た。 1) 提案した促進試験方法によって，常温下では見られなかった有機系接着剤の劣化性状が確認できることを示した。 2) 1）で劣化の確認された有機系接着剤は，屋外暴露試験でも良好な結果を得ることはできなかった。 3) 促進試験と屋外暴露試験ともに，有機系接着剤の経年劣化の傾向として，界面による破断が増加することや，破壊時エネルギーが小さくなることが確認された。したがって，促進試験によって屋外暴露試験で生じる劣化を捉えることができることを示唆していると考える。 超高層建築物におけるシーリング材の経年劣化を明らかにするため，促進耐候性試験および実際の超高層建築物の調査を実施し，経年劣化の検証を行った。今回の実験範囲の結果，以下の知見を得た。 1) 提案した促進試験方法によって，シーリング材の経年による伸び率は促進試験時間によって概ね直線的に低下することを示した。 2) 実際の超高層建築物の調査結果から，懸念されていた建築物高層階でのシーリング材の極端な劣化は見られず，シーリング材の劣化は主に経年劣化の影響をもとに予測すればよいことを示した。 3) 促進試験から超高層建築におけるシーリング材の劣化進行を安全側に評価できるものの，予測するにはさらなるデータの蓄積が必要であった。 以上の結果より，本論では建築物における外装材料の経年劣化の評価に関する研究として，現在の建築物で多用されている塗装された木材，塗装されたコンクリート，タイル仕上げ，およびそれらと併用されることの多いシーリング材の経年劣化を，促進試験で予測するための手法を考案し検証するとともに，屋外暴露試験や建築物で実際の経年劣化を検証し，それらの結果から経年劣化の予測を行い，本論の範囲内において各外装材料の経年劣化を明確にした。 |
|||||
| 言語 | ja | |||||
| 抄録 | ||||||
| 内容記述タイプ | Abstract | |||||
| 内容記述 | In recent years, with the promotion oflong·term use of buildings, the importance of prolonging the life and maintaining of exterior materials them is increasing. However, there are many types of exterior materials and the use of new materials is increasing in recent years, so research on the evaluation of aging deterioration is not sufficient. Therefore, I conducted study on the progression and evaluation of deterioration of painted wood, painted concrete, tile finishing, and sealing materials, which are widely used in modern buildings. We devised and verified a method for predicting aging deterioration of each material through accelerated tests, verified actual aging deterioration through outdoor exposure tests, etc., and tried to predict the actual aging deterioration based on these results. For wood materials, the progress of surface erosion and checks and the suppression effect of surface erosion and checks by various coatings were verified by accelerated weathering tests and outdoor exposure tests. For painted concrete, in order to clarify the carbonation suppression effect of water-based finishing materials on reinforced concrete structures, accelerated carbonation tests and outdoor exposure tests were conducted to verify the effectiveness. For tile finishing, in order to clarify the durability of the exterior wall tiling method using organic adhesives, accelerated deterioration tests (heat and cool cycling test) and outdoor exposure tests were conducted to verify the durability performance For sealing material, in order to clarify the aging deterioration of sealing materials in high ·rise buildings, accelerated weather tests and surveys of actual high·rise buildings were conducted to verify aging deterioration. Based on the above results, I devised and verified a prediction method using accelerated tests, verified aging deterioration using outdoor exposure tests and actual buildings, and predicted aging deterioration based on these results. Within the scope of this paper, the aged deterioration of each exterior material was clarified. |
|||||
| 言語 | en | |||||
| 学位名 | ||||||
| 言語 | ja | |||||
| 学位名 | 博士（工学） | |||||
| 学位授与機関 | ||||||
| 言語 | ja | |||||
| 学位授与機関名 | 東京工芸大学 | |||||
| 学位授与年度 | ||||||
| 内容記述タイプ | Other | |||||
| 内容記述 | 2023 | |||||
| 言語 | ja | |||||
| 学位授与年月日 | ||||||
| 学位授与年月日 | 2023-09-13 | |||||
| 学位授与番号 | ||||||
| 学位授与番号 | 32708甲第61号 | |||||